ASTM A213 T2 Alloy Steel Seamless Tubes
A213 T2 Seamless Steel Tube can prevent the tendency of graphitization, after long-term use at 480-540 ℃, the mechanical properties and microstructure are stable enough, and the pipe processing and welding properties are good.

Description

ASME SA213 T2 Seamless Steel Tubes

SA213 T2 is the steel grade in ASME SA213M standard. It is a 1 / 2cr-1 / 2Mo type steel developed on the basis of 1 / 2Mo steel. It is a ferritic hot strength steel for boiler and superheater.
SA213 T2 steel is close to 12CrMoG of GB5310 in China. Because the steel contains chromium, which can prevent the tendency of graphitization, after long-term use at 480-540 ℃, the mechanical properties and microstructure are stable enough, and the pipe processing and welding properties are good.

Equivalent steel grade

Standard Grade
ASME SA213 SA213 T2
GB5310 12CrMoG

ASTM A213 T2 Seamless Steel Tubes Quick Details
Manufacture:Seamless process ,Hot-finished or Cold-finished
Wall thickness(WT): 0.9 mm——12.7 mm.
Outer diameter (OD): 12.7 mm——127 mm
Length: 6M or specified length as required.
Ends: Plain End, Beveled End, Treaded

Additional Info
Port of Shipment: Tianjin, China
Payment Terms:T / T, LC
Delivery: 7-15 days after payment
Surface: Tubes will be varnished (Outside only) to prevent rust.
Marking: Standard + Steel Grade + Size + Heat No + Lot No
Package: Bundles (hexagonal),Wooden Boxes,Crates (steel/wooden) or as required

Application of ASME SA213 T2 seamless steel tubes
SA213 t2asme SA213 T2 seamless steel tubes are mainly used for superheater and reheater system with working temperature lower than 540 ℃, and also for water wall tube in supercritical boiler

Chemical composition (%)

 Grade        Chemical composition
C Si Mn P S Cr Mo
SA213 T2 0.10-0.20 0.10-0.30 0.30-0.61 ≤0.025 ≤0.025 0.50-0.81 0.44-0.65
12CrMoG 0.08-0.15 0.17-0.37 0.40-0.70 ≤0.035 ≤0.035 0.40-0.70 0.40-0.55

Metallographic structure
The delivery state of ASME SA213 T2 seamless steel tubes are normalizing and tempering, and the microstructure is ferrite + sorbite.

Mechanical properties
Mechanical properties at room temperature

Grade Mechanical properties at room temperature
Tensile strength Yield strength Elongation HardnessHB（HRB）
SA-213 T2 ≥ 415 ≥205 ≥ 30 ≤163(85)
12CrMoG 410-560 ≥205 ≥21

Oxidation resistance
SA213 T2 steel is mainly used in Superheater and reheater system with working temperature lower than 540 ℃, and its oxidation resistance is better than that of carbon steel and carbon manganese steel.